Product Details:
|
| Product Nmae: | Ferro Silicon Magnesium Alloy | Shape: | Lump,Granule |
|---|---|---|---|
| Material: | Si,Mg,RE,Ca,Al,Fe | Model Number: | FeSiMg8Re3,FeSiMg8Re5 |
| Feature: | An Improve The Molten Iron Purity | Usage: | Steel-making Cast Iron Deoxidizer |
| Highlight: | FeSiMg8Re Ferro Silicon Alloy,Ferro Silicon Alloy 7% Mg,Ferro silicon 7% Magnesium Alloy |
||
High Efficiency FeSiMg8Re Ferro Silicon Magnesium Deoxidizer
Ferro Silicon Magnesium Description
Ferro Silicon Magnesium is an alloy composed by melting ferrosilicon, calcium, magnesium, rare earth, etc. It is an excellent spheroidizing agent with strong deoxidation and desulfurization effects. Ferrosilicon, rare earth ore and magnesium metal are the main raw materials for the production of rare earth magnesium ferrosilicon. The production of rare earth magnesium ferrosilicon alloy is carried out in an arc furnace. The furnace consumes a lot of electricity and can also be manufactured using an intermediate frequency furnace.
Specifications FeSiMg
| Brand | Code |
Chemical Compositon (%)
|
|||||
| Mg | Re | Si | Ca | Al | Fe | ||
| FeSiMg6Re1 | 6-1 | 5.0-7.0 | 0.5-1.5 | 38-44 | 2.0-3.0 | <1.0 |
Balance
|
| FeSiMg7Re1 | 7-1 | 6.0-8.0 | 0.5-1.5 | 38-44 | 1.0-1.5 | <1.0 | |
| FeSiMg5Re2 | 5-2 | 4.0-6.0 | 1.0-3.0 | 38-44 | 2.0-3.0 | <1.0 | |
| FeSiMg7Re3 | 7-3 | 6.0-8.0 | 2.0-4.0 | 38-44 | 2.0-3.5 | <1.0 | |
| FeSiMg8Re3 | 8-3 | 7.0-9.0 | 2.0-4.0 | 38-44 | 2.0-3.5 | <1.0 | |
| FeSiMg8Re5 | 8-5 | 7.0-9.0 | 4.0-6.0 | 38-44 | 2.0-3.5 | <1.0 | |
| FeSiMg8Re7 | 8-7 | 7.0-9.0 | 6.0-8.0 | 38-44 | 2.0-3.5 | <1.0 | |
| FeSiMg10Re7 | 10-7 | 9.0-11.0 | 6.0-8.0 | 38-44 | 2.0-3.5 | <1.0 | |
Ferro Silicon Magnesium Feature
1. The spheroidization reaction kinetic conditions are good, the reaction is relatively stable, and the process performance of the impulse method is better.
2. Significantly improve the casting performance of ductile iron, increase its fluidity by 40% compared with magnesium ductile iron, reduce the formation temperature of rare earth magnesium nodularizer oxide film by about 50℃, reduce the expansion value before shrinkage by 0.3 to 0.4%, and make shrinkage and pinch Casting defects such as slag, subcutaneous pores and cold partition are reduced.
Packing & Delivery
Packing:1 Ton parcel, 1000kg/bag or as your detailed requirements
Shipping: within 15-20 days after receiving your advance payment or L/C
Our Services
We can try our best to provide you the good services as below:
1.We have Experienced staffs .
2.Provide kinds of certificates.
3.24 hours on line to answer all your questions .
4.The content packing particle size may be based on customer demand.
5.Quality can be guaranteed. we provide safe products to our users.